    EVA foam is closed cell foam made from Ethylene Vinyl Acetate and blended copolymers. It has a high level of chemical cross-linking. The result is a semi-rigid product with a fine uniform cell structure that is suitable for use in a wide variety of situations and applications. Benefits of EVA Foam include;

    • Impact and vibration absorption
    • Weather and chemical resistance including splash resistance to oils and fuels
    • Acoustic and thermal insulation properties
    • Buoyancy with low water absorption
    • Suitability for thermo-forming and thermo-molding

    EVA sheet is featured by its elasticity, duration, lightweight, skid and waterproof, easy to wash, and widely used in professional competition gyms mats, training gyms mats, school pool mats, school and amusement grounds mats. Its well accepted by the customers both at home and abroad because of its low price and good quality. 

    Item No.

    L-2500

    C-1600

    C-3000

    H-25

    H-35

    A-25

    Density
    (g/cm^3)

    0.021~0.027

    0.035~0.041

    0.023~0.029

    0.065~0.075

    0.07~0.08

    0.08~0.09

    Hardness
    (type C)

    15~21

    24~30

    7~13

    25~30

    30~35

    25~30

    Original Sheet Size
    (cm)

    100*200

    100*200

    100*200

    100*200

    100*200

    100*200

    Original Sheet Thickness
    (mm)

    80

    80

    80

    36

    32

    38

    Tensile Strength
    (kg/cm^2)

    2.0

    3.2

    2.8

    9.5

    11.8

    9.5

    Elongation at Break (%)

    180

    180

    340

    220

    160

    120

    Tear Strength (kg/cm)

    1.9

    2.4

    2.1

    3.4

    3.8

    3.3

    Compressive Strength
    at 25% Deflection
    (kg/cm^2)

    0.4

    0.6

    0.3

    0.7

    0.8

    0.7

    Compressive Strength
    at 50% Deflection
    (kg/cm^2)

    1.0

    1.3

    0.8

    1.5

    1.8

    1.6

    Compression Set
    to 50% of
    Original Thickness
    (%)

    10

    14

    17

    20

    20

    20

    Water Absorption
    (%, by weight,
    room temp., 5 hrs)

    < 1

    < 1

    < 1

    < 1

    < 1

    < 1

    Type

    PE/EVA

    PE/EVA

    EVA/PE

    EVA/PE

    EVA/PE

    EVA